华秀塑胶为您提供详细的Lexan PC BPL1000物性表参数。
想了解更多的与Lexan PC BPL1000相关的物性参数,请点击 LEXAN™ PC产品列表。
如果您对我们的Lexan PC BPL1000有任何疑问,或者想索取Lexan PC BPL1000 物性表datasheet、物质安全资料证书MSDS、ROHS检验报告、SGS报告、REACH环保证明、FDA证明、EU法规证明、UL证书及出厂证明COC/COA报告等,敬请拨打我们的服务热线 020-82582555,或者点击 联系我们 给我们留言。
[下载BPL1000物性表PDF]
Consult BPL1000
Lexan PC BPL1000 物性
BPL1000是注射模压级聚碳酸酯,无氯和非溴化阻燃UL - 94 V0(0.8mm),有各种不透明的颜色,理想的薄壁应用 |
Property |
TYPICAL PROPERTIES (1) | ||||
MECHANICAL |
Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min |
640 |
kgf/cm2 |
ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min |
520 |
kgf/cm2 |
ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min |
4.7 |
% |
ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min |
96.3 |
% |
ASTM D 638 | |
Tensile Modulus, 5 mm/min |
27300 |
kgf/cm2 |
ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
1040 |
kgf/cm2 |
ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span |
27100 |
kgf/cm2 |
ASTM D 790 | |
Tensile Stress, yield, 50 mm/min |
64 |
MPa |
ISO 527 | |
Tensile Stress, break, 50 mm/min |
53 |
MPa |
ISO 527 | |
Tensile Strain, yield, 50 mm/min |
4.7 |
% |
ISO 527 | |
Tensile Strain, break, 50 mm/min |
96.8 |
% |
ISO 527 | |
Tensile Modulus, 1 mm/min |
2460 |
MPa |
ISO 527 | |
Flexural Stress, yield, 2 mm/min |
94 |
MPa |
ISO 178 | |
Flexural Modulus, 2 mm/min |
2360 |
MPa |
ISO 178 | |
IMPACT |
Value | Unit | Standard | |
Izod Impact, notched, 23°C |
61 |
cm-kgf/cm |
ASTM D 256 | |
Izod Impact, notched, -30°C |
N/A |
cm-kgf/cm |
ASTM D 256 | |
Instrumented Impact Total Energy, 23°C |
495 |
cm-kgf |
ASTM D 3763 | |
Izod Impact, notched 80*10*4 +23°C |
17 |
kJ/m2 |
ISO 180/1A | |
Izod Impact, notched 80*10*4 -30°C |
12 |
kJ/m2 |
ISO 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
17 |
kJ/m2 |
ISO 179/1eA | |
THERMAL |
Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 |
111 |
°C |
ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed |
105 |
°C |
ASTM D 648 | |
CTE, -40°C to 40°C, flow |
7.E-05 |
1/°C |
ASTM E 831 | |
CTE, -40°C to 40°C, xflow |
7.E-05 |
1/°C |
ASTM E 831 | |
CTE, -40°C to 40°C, flow |
7.E-05 |
1/°C |
ISO 11359-2 | |
CTE, -40°C to 40°C, xflow |
7.E-05 |
1/°C |
ISO 11359-2 | |
Ball Pressure Test, 75°C +/- 2°C |
PASS |
- |
IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 |
112 |
°C |
ISO 306 | |
Vicat Softening Temp, Rate B/120 |
114 |
°C |
ISO 306 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
96 |
°C |
ISO 75/Af | |
Relative Temp Index, Elec |
80 |
°C |
UL 746B | |
Relative Temp Index, Mech w/impact |
80 |
°C |
UL 746B | |
Relative Temp Index, Mech w/o impact |
80 |
°C |
UL 746B | |
PHYSICAL |
Value | Unit | Standard | |
Specific Gravity |
1.16 |
- |
ASTM D 792 | |
Mold Shrinkage on Tensile Bar, flow (2) |
0.5 - 0.7 |
% |
SABIC Method | |
Mold Shrinkage, flow, 3.2 mm |
0.5 - 0.7 |
% |
SABIC Method | |
Mold Shrinkage, xflow, 3.2 mm |
0.5 - 0.7 |
% |
SABIC Method | |
Melt Flow Rate, 300°C/1.2 kgf |
25.2 |
g/10 min |
ASTM D 1238 | |
Density |
1.2 |
g/cm2 |
ISO 1183 | |
Water Absorption, (23°C/sat) |
0.35 |
% |
ISO 62 | |
Moisture Absorption (23°C / 50% RH) |
0.15 |
% |
ISO 62 | |
Melt Volume Rate, MVR at 300°C/1.2 kg |
23 |
cm210 min |
ISO 1133 | |
ELECTRICAL |
Value | Unit | Standard | |
Dielectric Strength, in oil, 1.6 mm |
27 |
kV/mm |
ASTM D 149 | |
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 | |
Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 | |
Relative Permittivity, 50/60 Hz |
3 |
- |
IEC 60250 | |
Relative Permittivity, 1 MHz |
2.9 |
- |
IEC 60250 | |
Dissipation Factor, 50/60 Hz |
0.03 |
- |
IEC 60250 | |
Dissipation Factor, 1 MHz |
0.01 |
- |
IEC 60250 | |
Comparative Tracking Index |
200 |
V |
IEC 60112 | |
FLAME CHARACTERISTICS |
Value | Unit | Standard | |
UL Recognized, 94V-2 Flame Class Rating (3) |
0.45 |
mm |
UL 94 | |
UL Recognized, 94V-0 Flame Class Rating (3) |
0.8 |
mm |
UL 94 | |
Glow Wire Flammability Index 960°C, passes at |
1 |
mm |
IEC 60695-2-12 | |
Glow Wire Ignitability Temperature, 1.0 mm |
800 |
°C |
IEC 60695-2-13 | |
Oxygen Index (LOI) |
36 |
% |
ISO 4589 |
Processing |
Parameter | ||
Injection Molding |
Value | Unit |
Drying Temperature |
90 |
°C |
Drying Time |
4 |
hrs |
Maximum Moisture Content |
0.02 |
% |
Melt Temperature |
280 - 300 |
°C |
Nozzle Temperature |
270 - 290 |
°C |
Front - Zone 3 Temperature |
280 - 300 |
°C |
Middle - Zone 2 Temperature |
270 - 290 |
°C |
Rear - Zone 1 Temperature |
260 - 280 |
°C |
Hopper Temperature |
60 - 80 |
°C |
Mold Temperature |
90 |
°C |
相关搜索: BPL1000-111 BPL1000-701 BPL1000-BK1066 BPL1000-NA Lexan BPL1000 BPL1000物性 Sabic BPL1000 GE BPL1000 PC BPL1000 Sabic PC PC 工程塑料 聚碳酸酯PC PC 物性
广州华秀塑胶有限公司不仅是专业的Lexan PC BPL1000原料供应商,亦注重技术支持及全方位的解决方案,提供从材料鉴定、模具设计、成型加工等系列帮助,亦可为客户量身定制各特殊性能之Lexan PC BPL1000材料,进而协助客户提高产品竟争力。
地址:广州市天河区中山大道中439号东圃天银商贸大厦1720-1723室
电话:020-82582555
传真:020-82523699
Email: sales@va-so.cn
Lexan PC BPL1000报价 >>
常规产品
长纤增强尼龙6 长纤增强PP
长纤增强复合材料 冲击改性复合尼龙66
冲击改性复合尼龙6 高强尼龙
冲击改性复合尼龙 冲击改性复合材料
改性PP 改性的合金料
高温改性塑料 含氟聚合物
改性POM 改性PBT
改性PC 焊接用复合塑料
高比重复合塑料 永久防静电塑料
永久防静电ABS 永久防静电合金
永久防静电POM 其他导电材料
导电尼龙 导电PE,导电PP
高温导电塑料 导电POM
导电PBT 导电PC
其他非PTFE自润滑塑料 非PTFE自润滑PA
非PTFE自润滑聚苯醚 非PTFE自润滑PPA
非PTFE自润滑聚甲醛 非PTFE自润滑聚碳酸酯
其他润滑塑料 润滑尼龙
润滑烯烃 润滑PPO(PPE+PS)
耐热润滑塑料 润滑POM
润滑PBT 润滑弹性体
润滑PC 挤出PBT
热传导复合塑料 其他PC
EMI/RFI屏蔽复合塑料 预着色非填充树脂
热门工程塑胶原料
Lexan_BFL2200 DF006 IX95700 AX02747 MFB429 LTX300A DCL36 141 Noryl_FM4025 LCL33 HFG25Z IF006S R1000JX4 DFL34EH RFZ22S NORYL™ PPO  LEXAN™ PC  VALOX™ PBT  ULTEM™ PEI  CYCOLOY™ PC/ABS  XYLEX™ PC/PET  XENOY™ PC/PBT/PET  Noryl GTX PPE/PA  CYCOLAC™ ABS  GELOY™ ASA  Colorcomp  Faradex  Konduit  Lubricomp  Lubriloy  Stat-kon  Stat-loy  Thermocomp  Thermotuf  Verton