Lexan PC BFL2015物性表 - GE BFL2015, Sabic BFL2015, BFL2015塑料, Lexan PC BFL2015

华秀塑胶为您提供详细的Lexan PC BFL2015物性表参数。

想了解更多的与Lexan PC BFL2015相关的物性参数，请点击 LEXAN™ PC产品列表。

如果您对我们的Lexan PC BFL2015有任何疑问，或者想索取Lexan PC BFL2015 物性表datasheet、物质安全资料证书MSDS、ROHS检验报告、SGS报告、REACH环保证明、FDA证明、EU法规证明、UL证书及出厂证明COC/COA报告等，敬请拨打我们的服务热线 020-82582555，或者点击联系我们给我们留言。

GE工程塑胶物性目录 >> LEXAN™ PC >> BFL2015 物性表

[下载BFL2015物性表PDF] Consult BFL2015

Lexan PC BFL2015 物性

无溴无氯阻燃剂的PC 。 15 ％玻璃纤维增强的PC 。只有不透明的颜色.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	930	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	920	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3.5	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	4	%	ASTM D 638
Tensile Modulus, 5 mm/min	54300	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	1590	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	46900	kgf/cm2	ASTM D 790
Tensile Stress, yield, 50 mm/min	103	MPa	ISO 527
Tensile Stress, break, 50 mm/min	100	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.6	%	ISO 527
Tensile Strain, break, 50 mm/min	4.3	%	ISO 527
Tensile Modulus, 1 mm/min	4950	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	150	MPa	ISO 178
Flexural Modulus, 2 mm/min	4280	MPa	ISO 178
IMPACT	Value	Unit	Standard
Charpy Impact, unnotched, 23°C	67	kJ/m2	ISO 179/2C
Charpy Impact, unnotched, -30°C	75	kJ/m2	ISO 179/2C
Izod Impact, notched, 23°C	7	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	N/A	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy, 23°C	622	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	80	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	80	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	8	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	7	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	8	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	6	kJ/m2	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	100	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	100	kJ/m2	ISO 179/1eU
Charpy Impact, notched, 23°C	12	kJ/m2	ISO 179/2C
Charpy Impact, notched, -30°C	8	kJ/m2	ISO 179/2C
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	148	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	145	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	141	°C	ASTM D 648
CTE, -30°C to 30°C, flow	4.E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	4.E-05	1/°C	ASTM D 696
CTE, 23°C to 80°C, flow	4.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	4.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES0	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	149	°C	ISO 306
Vicat Softening Temp, Rate B/120	150	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	132	°C	ISO 75/Af
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.23	-	ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2)	0.2 - 0.5	%	SABIC Method
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.5	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.2 - 0.5	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	6.5	g/10 min	ASTM D 1238
Density	1.3	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	6	cm210 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Dielectric Strength, in oil, 1.6 mm	20	kV/mm	ASTM D 149
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
Relative Permittivity, 50/60 Hz	3.2	-	IEC 60250
Relative Permittivity, 1 MHz	3.1	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.02	-	IEC 60250
Dissipation Factor, 1 MHz	0.01	-	IEC 60250
Comparative Tracking Index	150	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.5	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	825	°C	IEC 60695-2-13
Oxygen Index (LOI)	38	%	ISO 4589

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 310	°C
Rear - Zone 1 Temperature	270 - 300	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C

[下载BFL2015物性表PDF] Consult BFL2015

相关产品物性: LF1520A 503R 500R SP7602 500ECR 3412R SP7604 3414R 3413R BFL2010 3412ECR 500 503

广州华秀塑胶有限公司不仅是专业的Lexan PC BFL2015原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之Lexan PC BFL2015材料，进而协助客户提高产品竟争力。

联络我们

地址:广州市天河区中山大道中439号东圃天银商贸大厦1720-1723室

电话:020-82582555

传真:020-82523699

Email: sales@va-so.cn

Lexan PC BFL2015报价 >>

常规产品

长纤增强尼龙66 长纤增强PPA
长纤增强尼龙6 长纤增强PP
长纤增强复合材料冲击改性复合尼龙66
冲击改性复合尼龙6 高强尼龙
冲击改性复合尼龙冲击改性复合材料
改性PP 改性的合金料
高温改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用复合塑料
高比重复合塑料永久防静电塑料
永久防静电ABS 永久防静电合金
永久防静电POM 其他导电材料
导电尼龙导电PE,导电PP
高温导电塑料导电POM
导电PBT 导电PC
其他非PTFE自润滑塑料非PTFE自润滑PA
非PTFE自润滑聚苯醚非PTFE自润滑PPA
非PTFE自润滑聚甲醛非PTFE自润滑聚碳酸酯
其他润滑塑料润滑尼龙
润滑烯烃润滑PPO(PPE+PS)
耐热润滑塑料润滑POM
润滑PBT 润滑弹性体
润滑PC 挤出PBT
热传导复合塑料其他PC
EMI/RFI屏蔽复合塑料预着色非填充树脂